Steel case vs Brass case - reloading

[Defcon09]

That seems to be the rest of the story. Not malleable enough with the die pressure. I'm always interested if someone can make it work, but right now its a a fail.FIRST ATTEMPT I LEARNED!

I am thinking about making a jig with a hole the size needed to resize the neck. This will be made from UHMW or HDPE to see if the case is easily removed.

[registror]

Not new to reloading but am new to loading steel cases vs brass cases. Me and my boys have moved over to 223 AR caliber and was given a few different brands to break the gun in. Among these were a box of WOLF and TCW steel cases, nothing new there but, both are using boxer primers. I managed to pick up a box of TulAmmo small rifle primers at a good price. But, the box does not indicate if they were boxer or berdan. Since the box says "small rifle" I assume they were boxer. Fast forward - - - after shooting some brass and steel ammo I decided to look into reloading a few rounds of the steel stuff. Looks like nothing unusual. Primers fit so decided to try some of the brass cases. However, only 1 round of 10 allowed the primer to insert under normal squeeze using a Lee hand prime tool. After a few rounds of frustration I decided to measure the diameter of the primer and primer hole in both materials. The sr primers measured .0015 +/- larger than the primer hole in the brass. Evidently the TulAmmo primers are made for the steel cases and not the brass (USA made?) I tool a few brass cases and removed about .001" or just enough for the primer to insert under a firm but good install. Since then both the steel and brass rounds shot fine. On another note I did find the steel cases did not want to resize as easily as the brass case. I had to make small adjustments in the die to get the neck opening to resize and still used a lot of force on the handle! Thoughts and suggestions...……...

I would think that the steel cases would wear out your reloading dies in short order. Every range I've ever gone to had brass 223 cases and 9mm cases laying everywhere, so I dont think that there's a shortage of either. I've always heard that sizing the steel cases removes the coating that keeps them from rusting and seizing up in your chamber, so I'd avoid reloading them. They are likely to cause breakage of your extractor/ejector. One if the cases are too hard to extract, the other if lube the chamber walls and the cases extract too easily.

[Armyjimbo]

Registror that's correct , however the weak point in the system is primer availability. I saw what happened last election, and stocked upon those. Brass can be salvaged (I do a lot of picking up at the range), powders can be switched, bullets can be cast. But primers unless your willing to really go down the rabbit hole are a 1 time use commodity. I have seen successful reuse of them on YOUTUBE but like reloading .22lr it really is a lot of effort.

[registror]

hth do I start a new topic on this site? I dont see a way to do so?

[Armyjimbo]

SUBSCRIBE

• TOPICS
• LATEST ACTIVITY
• MY SUBSCRIPTIONS
• PHOTOS

• New Topic

If you go to the forum topic it should be in look for this it has the new topic button right there

[registror]

just tried it and the message is "you are not authorized to use this page"

[Garand]

Decades ago I tried to reload steel .45 acp casings back when I was shooting IPSC, I found that I was never able to get a crimp that would hold tight.